Aluminium 2017 (UNS A92017 / DIN 3.1325 / EN AW-2017) 2.0 mm Sheets & Plates Manufacturer, Supplier, Exporter & Stockist in India for Aerospace & Engineering Applications
Vintex Steel & Engg. Co. is a reputable Aluminium 2017 2.0 mm Sheets and Plates manufacturer, which is engineered to meet the highest quality standards with regard to strength, precision and high machinability. The sheets are very much applicable in aerospace, automobile, marine and engineering products, whereby high performance and reliability are the key factors. Through its 2017 grade, aluminium offers an excellent combination of hardness and corrosion resistance, the grade is suitable for parts that require durability and at the same time. Every sheet is made with care to the high standards of quality, with a good finish on the surface and precision in dimensions.
Grade Table Suitable For Aluminium 2017 – 2.0 mm Sheets & Plates.
| Standard | Grade / Designation | Equivalent Grades | Product Form | Thickness |
|---|---|---|---|---|
| UNS | A92017 | DIN 3.1325, EN AW-2017 | Sheets & Plates | 2.0 mm |
| EN | EN AW-2017 | UNS A92017, DIN 3.1325 | Sheets & Plates | 2.0 mm |
| DIN | 3.1325 | UNS A92017, EN AW-2017 | Sheets & Plates | 2.0 mm |
| ISO | AlCu4MgSi | EN AW-2017, UNS A92017 | Sheets & Plates | 2.0 mm |
Highlights of Aluminium 2017 - 2.0 mm Sheets and Plates
- High Mechanical Strength: Aluminium 2017 is appropriate for high-load structural applications due to its exceptional tensile and yield strengths.
- Superior Machinability: The alloy's smooth surface finish and ease of machining make it perfect for precision engineering components.
- Excellent Fatigue Resistance: Functions dependably under cyclic load, particularly in automotive and aerospace components.
- Lightweight Material: Provides a strong strength-to-weight ratio, helping reduce overall component weight.
- Heat Treatable Alloy: By using the right heat treatment techniques, mechanical qualities can be improved.
- Good Thermal Conductivity: It is appropriate for thermal and structural applications due to its effective heat dissipation.
- Dimensional Accuracy: Tight thickness tolerances are provided for 2.0 mm sheets and plates to ensure reliable performance.
- Grade for Aerospace and Engineering: extensively utilised in high-performance technical components, tooling plates, and aircraft structures.
Chemical Composition of Aluminium 2017 (UNS A92017)
| Element | Composition (%) |
|---|---|
| Copper (Cu) | 3.5 – 4.5 |
| Magnesium (Mg) | 0.4 – 0.8 |
| Silicon (Si) | 0.2 – 0.8 |
| Manganese (Mn) | 0.4 – 1.0 |
| Iron (Fe) | ≤ 0.7 |
| Zinc (Zn) | ≤ 0.25 |
| Titanium (Ti) | ≤ 0.15 |
| Aluminium (Al) | Balance |
Mechanical Properties of Aluminium 2017 – 2.0 mm Sheets & Plates
| Property | Typical Value |
|---|---|
| Tensile Strength | 370 – 460 MPa |
| Yield Strength | 210 – 290 MPa |
| Elongation | 8 – 15% |
| Hardness | 105 – 135 HB |
| Density | 2.78 g/cm³ |
| Melting Point | 510 – 640°C |
| Thermal Conductivity | 134 W/m·K |
Aluminium 2017 - 2.0 mm Sheets and Plates are high-strength, heat-treatable aluminium alloys with good mechanical characteristics and machinability. With a high copper concentration, this alloy has excellent strength-to-weight performance, making it a popular choice for aerospace, automotive, and precision engineering applications. The 2.0 mm thickness assures dimensional correctness and homogeneity, making it suitable for use in structural components, tooling plates, and high-load assemblies where durability, fatigue resistance, and lightweight properties are critical.
Equivalent Grades of Aluminium 2017 - 2.0 mm Sheets and Plates
| Standard | Equivalent Grade |
|---|---|
| UNS | A92017 |
| EN | EN AW-2017 |
| DIN | 3.1325 |
| ISO | AlCu4MgSi |
Aluminium 2017-2.0 mm Sheets & Plates are ideal for dynamic and high-performance situations because of their exceptional fatigue resistance and stability under repetitive stress. Consistent performance in demanding engineering applications is ensured by the alloy's capacity to retain strength under high temperatures. Its high thermal conductivity makes it even more suitable for usage in parts like structural panels and mechanical housings that need efficient heat dissipation.
Furthermore, Aluminium 2017 sheets and plates have dependable formability and may be easily machined into complex shapes with tight tolerances. While the alloy has modest corrosion resistance, it can be improved with surface treatments such as anodising or cladding. These properties make 2.0 mm Aluminium 2017 sheets and plates an adaptable alternative for aircraft structures, transportation systems, tooling, and industrial fabrication.
Type of Sub-products

Aluminium 2017 T4 Sheets & Plates Aluminium 2017 T4 Sheets & Plates
These sheets and plates are solution heat treated and naturally aged to the T4 temper, offering an excellent balance of strength, machinability, and formability.

Aluminium 2017 T6 Sheets & Plates Aluminium 2017 T6 Sheets & Plates
The T6 temper variant is artificially aged after heat treatment, resulting in higher tensile strength and superior hardness.